AgNi10 / Hera 367

  • General Designation: AgNi10
  • Applications: sliding contacts, contacts
  • Product Forms: wire, strip
  • Density (g/cm³): 10.3

Details

Age Hardenable
No
Material Behaviour
ductile
Forming Process
formable, machinable, can be roll clad

Corrosion Resistant
sensitive to sulphur

IACS Min. (%) [100% IACS ≙ 58 S*m/mm²]
81.9
IACS Max. (%) [100% IACS ≙ 58 S*m/mm²]
86
Thermo-emf. vs. copper Hard (mV)
0.18
Temperature coefficient of electric resistivity
From Temperature (°C)
To Temperature (°C)
Hard (x10-4/K)
Annealed (x10-4/K)
0 100 28.9 32.4

Young's Modulus (GPa)
84
Property Range
Hardness (HV)
Tensile Strength (MPa)
Yield Strength (MPa)
Elongation (%)
50 - 90

Melting Range
From Temperature (°C)
To Temperature (°C)
960 1455
Linear Coefficient of Expansion³
From Temperature (°C)
To Temperature (°C)
Coefficient (x10-6/K)
20 100 18.34
20 200 18.75
20 300 19.19
20 400 19.76
20 500 20.32
20 600 20.83
20 700 21.36
20 800 21.81
20 900 22.94
100 200 19.07
200 300 19.98
300 400 21.37
400 500 22.45
500 600 23.3
600 700 24.42
700 800 24.94
800 900 31.69

Disclaimer

The information in this data sheet contains only general information on the use of our products or examples for their application. They do not release the customer from a careful inspection of the delivered product for its fitness for the customer's particular purpose of use. Any customer's special requests regarding the particular use of a product will only be authoritative if Heraeus has confirmed to the customer in writing at the time of conclusion of a corresponding contract that the product delivered is fit for the customer's intended use. Heraeus, therefore, does not guarantee the correctness and completeness of the information regarding the customer's intended use. The customer's purchase will be governed exclusively by the written order confirmation of Heraeus and the Heraeus General Terms of Sale and Delivery, which are available at www.heraeus.com/gtc. This data sheet may be subject to changes at any time.

www.heraeus-precious-metals.com

Discuss your solution

Get in contact with experts to discuss further steps to find the optimal solution for your process.