PtIr30 / Hera 175

  • General Designation: PtIr30
  • Applications: Medical wire
  • Product Forms: wire
  • Density (g/cm³): 21.73

Details

Age Hardenable
Yes
Material Behaviour
ductile
Forming Process
formable, machinable, can be roll clad

Corrosion Resistant
corrosion resistant
Comment
oxidation resistant to 1000°C

IACS Min. (%) [100% IACS ≙ 58 S*m/mm²]
4.91
IACS Max. (%) [100% IACS ≙ 58 S*m/mm²]
5.06
Temperature coefficient of electric resistivity
From Temperature (°C)
To Temperature (°C)
Hard (x10-4/K)
Annealed (x10-4/K)
0 100 5.8 6.4

Young's Modulus (GPa)
300
Modulus of Rigidity (GPa)
97
Property Range
Hardness (HV)
Tensile Strength (MPa)
Yield Strength (MPa)
Elongation (%)
260 - 380 900 - 1100 700 - 1100 1 - 20

Melting Range
From Temperature (°C)
To Temperature (°C)
1900 1930
Linear Coefficient of Expansion³
From Temperature (°C)
To Temperature (°C)
Coefficient (x10-6/K)
20 100 7.6
20 200 8.2
20 300 8.6
20 400 8.8
20 500 8.9
20 600 9

Disclaimer

The information in this data sheet contains only general information on the use of our products or examples for their application. They do not release the customer from a careful inspection of the delivered product for its fitness for the customer's particular purpose of use. Any customer's special requests regarding the particular use of a product will only be authoritative if Heraeus has confirmed to the customer in writing at the time of conclusion of a corresponding contract that the product delivered is fit for the customer's intended use. Heraeus, therefore, does not guarantee the correctness and completeness of the information regarding the customer's intended use. The customer's purchase will be governed exclusively by the written order confirmation of Heraeus and the Heraeus General Terms of Sale and Delivery, which are available at www.heraeus.com/gtc. This data sheet may be subject to changes at any time.

www.heraeus-precious-metals.com

Discuss your solution

Get in contact with experts to discuss further steps to find the optimal solution for your process.