• Paste Type: LTCC
  • Application Method: Screen Printing
  • Substrate: LTCC
  • Metal: Ag
  • Application: LTCC
  • Description: TC2307 is a pure Ag conductor with low resistivity and superior fine line print resolution. TC2307 provides excellent compatibility with low temperature co-fired ceramic (LTCC) during the co-firing process.TC2307 is optimized for screen printing as a routing conductor. The material may readily be used to print fine line patterns.
  • Key features: Low resistivity provides low line loss at microwave frequencies#Compatible with LTCC#Prints fine line patterns
  • Process Temperature: 870-880 °C peak temperature Ramp from burnout to firing peak: 5 °C/minute. Dwell time at peak: up to 30 minutes. Total cycle time up to 12 hours (Most easily achieved in a box oven).
  • Viscosity: 125-225 Kcps Brookfield HBTSC4-14 spindle, 6R utility cup at 10 rpm, 25 °C