- General Designation: PdCu15
- Applications: sliding contacts, contacts
- Product Forms: wire, strip
- Density (g/cm³): 11.39
PdCu15 / Hera 614
Details
- Forming Process
- can be roll clad
- Comment
- corrosion resistant
- IACS Min. (%) [100% IACS ≙ 58 S*m/mm²]
- 4.27
- IACS Max. (%) [100% IACS ≙ 58 S*m/mm²]
- 4.32
- Thermo-emf. vs. copper Hard (mV)
- -1.9
- Temperature coefficient of electric resistivity
-
From Temperature (°C)To Temperature (°C)Hard (x10-4/K)Annealed (x10-4/K)
0 100 3.4 5
- Young's Modulus (GPa)
- 172
- Modulus of Rigidity (GPa)
- 50
- Property Range
-
Hardness (HV)Tensile Strength (MPa)Yield Strength (MPa)Elongation (%)
110 - 240 400 - 780 200 - 750 > 20
- Melting Range
-
From Temperature (°C)To Temperature (°C)
1370 1400 - Linear Coefficient of Expansion³
-
From Temperature (°C)To Temperature (°C)Coefficient (x10-6/K)
20 100 11.76 20 200 12.31 20 300 12.61 20 400 12.87 20 500 13.16 20 600 13.42 20 700 13.62 20 800 13.81 100 200 12.79 200 300 13.18 300 400 13.58 400 500 14.11 500 600 14.65 600 700 14.83 700 800 15.36
Disclaimer
The information in this data sheet contains only general information on the use of our products or examples for their application. They do not release the customer from a careful inspection of the delivered product for its fitness for the customer's particular purpose of use. Any customer's special requests regarding the particular use of a product will only be authoritative if Heraeus has confirmed to the customer in writing at the time of conclusion of a corresponding contract that the product delivered is fit for the customer's intended use. Heraeus, therefore, does not guarantee the correctness and completeness of the information regarding the customer's intended use. The customer's purchase will be governed exclusively by the written order confirmation of Heraeus and the Heraeus General Terms of Sale and Delivery, which are available at www.heraeus.com/gtc. This data sheet may be subject to changes at any time.
Discuss your solution
Get in contact with experts to discuss further steps to find the optimal solution for your process.