PtRh30 / Pt-30%Rh

  • General Designation: PtRh30
  • Applications: thermocouples, heating elements, resistance thermometers, anemometers
  • Product Forms: wire
  • Density (g/cm³): 17.6

Details

Material Behaviour
limited ductility

IACS Min. (%) [100% IACS ≙ 58 S*m/mm²]
8.9
IACS Max. (%) [100% IACS ≙ 58 S*m/mm²]
9.3
Thermo-emf. vs. copper Hard (mV)
-0.14
Temperature coefficient of electric resistivity
From Temperature (°C)
To Temperature (°C)
Hard (x10-4/K)
Annealed (x10-4/K)
0 100 13 14

Young's Modulus (GPa)
276
Young's Modulus - HT¹
Modulus of Rigidity (GPa)
95
Yield Strength RP0,2 - HT²
Ult. Tensile Strength Rm - HT³
Tensile Fracture Elongation A - HT⁴
Creep Rupture⁶
Property Range
Hardness (HV)
Tensile Strength (MPa)
Yield Strength (MPa)
Elongation (%)
150 - 300 500 - 1000 200 - 950 > 25
Sources Mechanical
⁶ measured and extrapolated

Melting Range
From Temperature (°C)
To Temperature (°C)
1920 1925

Disclaimer

The information in this data sheet contains only general information on the use of our products or examples for their application. They do not release the customer from a careful inspection of the delivered product for its fitness for the customer's particular purpose of use. Any customer's special requests regarding the particular use of a product will only be authoritative if Heraeus has confirmed to the customer in writing at the time of conclusion of a corresponding contract that the product delivered is fit for the customer's intended use. Heraeus, therefore, does not guarantee the correctness and completeness of the information regarding the customer's intended use. The customer's purchase will be governed exclusively by the written order confirmation of Heraeus and the Heraeus General Terms of Sale and Delivery, which are available at www.heraeus.com/gtc. This data sheet may be subject to changes at any time.

www.heraeus-precious-metals.com

Discuss your solution

Get in contact with experts to discuss further steps to find the optimal solution for your process.